recycle black bottle HDPE
Black bottle HDPE is widely used as the raw materials of plastic products.
Black bottle HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.
| film grade | |||
| Item | Test condition | Test Method | Value |
| Density (g/cm3) | ISO 1183 | 0.944-0.955 | |
| MFR (g/10min) | 190°C/2.16kg | ISO 1133 | 0.03-0.07 |
| Tensile strength at yield(Mpa) | ISO 527-2 | 22 | |
| Elongation at break(%) | ISO 527-2 | >350 | |
| ESCR (h) | F50,50°C,100% | ASTM D-1693A | 1000 |
| VICAT( °C ) | ASTM D-1525 | 126 |
| blown grade | |||
| Item | Test Condition | Test Method | Value |
| Density (g/cm) | ISO 1183 | 0.950~0.955 | |
| MFR (g/10min) | 190°C/2.16kg | ISO 1133 | 1.7~2.5 |
| Tensile strength at yield (Mpa) | ISO 527-2 | 24 | |
| Elongation at break(%) | ISO 527-2 | >600 |
| injection grade | |||
| Item | Test Condition | Test Method | Value |
| MFR (g/10min) | 190°C/2.16kg | ASTM D-1238 | 20 |
| Density (g/cm3) | --- | ASTM D-792 | 0.954 |
| Tensile strength at yiled(Mpa) | --- | ASTM D-638 | 28 |
| Elongation at break(%) | --- | ASTM D-638 | 250 |
| Impact tensile strength (kJ/m2) | --- | ASTM D-1822 | 42 |
| ESCR | ASTM D-1693 | 3 | |
| VACIT(°C ) | --- | ASTM D-1525 | 127 |
recycle black bottle HDPE