reinforced toughened impact resistant PA6
1 high strength 2 reinforced 3 toughened 4 glass fiber 5 impact resistant
reinforced with glass fiber , low water absorbtion rate. High streng with glass fiber
| Performance | Test condition | Testing standard | Units | B2HG6 |
| Mechanical property | ||||
| Tensile strength | 5mm/min | ISO527-1/2 | Mpa | 155 |
| Elongation at break | 5mm/min50mm/min | ISO527-1/2 | % | 3 |
| Bending modulus | 2mm/min | ISO178 | Mpa | 7000 |
| Bending strength | 2mm/min | ISO178 | Mpa | 220 |
| Charpy notched impact strength | 23°C | ISO179/leA | KJ/m2 | 15 |
| Charpy unnotched impact strength | 23°C | ISO179/leA | KJ/m2 | 70 |
| Thermal | ||||
| Melting | DSC.10K/min | ISO3146 | °C | 225 |
| Heat distortion temp. A | 1.8Mpa | ISO75 | °C | 220 |
| Heat distortion temp. B | 0.45Mpa | ISO75 | °C | 235 |
| Electrical property | ||||
| Surface resistivity | IEC60093 | Ohm | 1/0.1 | |
| Volume resistivity | IEC60093 | Ohm×cm | 10/0.1 | |
| Anti-arc-track of | TestotutionA | IEC60012 | V | |
| Physical property | ||||
| Density | 23°C | ISO1183 | g/cm3 | |
| Hygroscopicity | 23°C,50%r.h | ISO62 | % | 1.0 |
| Absorbent/water absorption | 23°C/saturtion | ISO62 | % | |
| Radial shrinkage | flow | ISO294-4 | % | |
| Transverse shrinkage | transverse | ISO294-4 | % | |
| Flame retardant | ||||
| Flammability test | 1.6/3.0mm | |||
| The level of flame-retardant test | 1mm thickness | UL94 | ||
| Material description | PA6+30%GF | |||
reinforced toughened impact resistant PA6