Product Description

-A two pack zinc pigmented ethyl silicate shop primer

-VOC less than 645g/L

Intended Uses

-A shop primer for the protection of steel

-Long term weathering protection

-Good welding and cutting performances

-Low health hazard

Product Information

Volume Solids

28%±2%

Finish/Sheen

Matt

Typical Film Thickness

15microns dry (53.5microns wet)

Theoretical Coverage

18.7m2/L at typical film thickness

Mix ratio

1:1(volume)2.3:1(mass)

Method of Application

Airless Spray

Recommended

Tip size range

0.38-0.53mm

Output pressure

≥15MPa

Air Spray

Tip size range

1.5-2.0mm

Output pressure

≥0.4MPa

Brush/Roller

For small area only

Thinner

Not recommended. Use only in exceptional circumstances (volume 5%)

Cleaner

X-107

Induction Period

Not necessary

Drying Information

10°C

25°C

35°C

Touch Dry

10min

5min

3min

Pot Life

7h

6h

5h

Overcoating Data           Substrate Temperature

Overcoated by

10°C

25°C

35°C

Min Max

Min Max

Min Max

Note: Consult Sunrui company, minimum of 24 hours for appropriate primers

Storage

Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Part A has a shelf life of 12 months minimum at 25°C, and 6 months minimum to Part B at the same condition. Subject to re-inspection thereafter.

Pack Size

Part A

20.5kg/10L in 20 L container

Part B

8.9kg/10L in 10 L container

Flash Point

Part A

Greater than 14°C

Part B

Greater than 14°C

Mixed paint

Greater than 14°C

Systems and

Compatibility

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

Surface Preparation

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

Steel surface should be prepared to Sa2.5(GB/T 8923-1988), using automatic blasting/spraying equipment.

Steel grit or a mixture of steel grit of particle size 0.6-1.0mm and steel shot of particles size 0.6-1.4mm are normally used to give a appropriate coarseness.

Apply 725-E47 before oxidation occurs. If oxidation has occurred, the entire oxidized area should be reblasted to the standard specified above.

Limitations

Drying time will depend on the substrate temperature and ventilation. If the relative humidity is below 50%, cure will be retarded.

725-E47 is not recommended for use as touch-up primer after fabrication.

Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.

Duty statement

The data in the sheet base on the information from the laboratory and practice. The application may exceed the control, so we only ensure our product quality. We own the right of the data sheet modification without informing.