Product

 Description

-A two pack epoxy heavy-duty anticorrosive coating and it is characterized by good adhesion and excellent resistance to chemicals, water and corrosion.

-VOC less than 180g/L

Intended Uses

-For use in heavy-duty anticorrosive areas.

-For steel or tidal range zone of concrete stakes heavy-duty anticorrosion.

-For interior circulatory water piles of power plant special strengthening anticorrosion

-For interior wall of steel pipes and concrete of Sewage treatment works, power plants and chemical plants etc. heavy-duty anticorrosion.

-For works of tap water and water anticorrosion

Product Information

Volume Solids

78%±2%

Finish/Sheen

Semi-Gloss

Typical Film Thickness

500 microns dry (640microns wet)

Theoretical Coverage

1.6m2/L at typical film thickness

Mix ratio

3.4:1(volume)7:1(mass)

Method of Application

Airless Spray

Recommended

Tip size range

0.45-0.68mm

Output pressure

≥17MPa

Air Spray

Not recommended

Brush/Roller

For small area only

Thinner

Not recommended. Use HX-501 only in exceptional circumstances (volume 5%)

Cleaner

HX-501

Induction Period

Not necessary

Drying Information

-5°C

5°C

25°C

35°C

Touch Dry

4h

2h

1h

45min

Hard Dry

48h

36h

20h

10h

Pot Life

4h

2h

1h

40min

Overcoating Data         Substrate Temperature

Overcoated by  

725-H45-ZF101G

-5°C

5°C

25°C

35°C

Min Max

Min Max

Min Max

Min Max

48h 14d

36h 10d

20h 7d

10h 5d

725-J43-5

48h -

36h -

20h -

10h -

Storage

Store in cool and dry conditions. Well ventilate. Keep away from hot and fire. Shelf Life: 12 months minimum at 25°C. Subject to re-inspection thereafter

Pack Size

Part A

30kg/15.5L in 20L container

Part B

4.3kg/4.5L in 6L container

Flash Point

Part A

Greater than 31°C

Part B

Greater than 29°C

Mixed paint

Greater than 31°C

Systems and

Compatibility

Consult your Sunrui Representative for the systems best suited for the surfaces to be protected.

Surface Preparation

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning. All surfaces to be coated should be clean, dry and free from contamination.

steel

Remove weld spatter and smooth weld seams and sharp edges. The surfaces should be blast cleaned to Sa2.5(GB/T 8923-1988).The weld seams areas could be cleaned to St3(GB/T 8923-1988)using power tool.

Apply 725-H45-ZF101G before oxidation occurs. If oxidation has occurred, the entire oxidized area should be reblasted to the standard specified above.

concrete

Remove loose powder of the cement, attached organisms, mud, oil or grease and other foreign matter thoroughly.

The surface can be abrade by blasting or using power tool to remove loose powder, attached organisms, mud etc. and oil can be cleaned by scour.

Repair/Maintenance

steel

The areas to be repaired should be cleaned to St3(GB/T 8923-1988)by  mechanical method or higher level of surface prepared to Sa2.5(GB/T 8923-1988)by abrasive blasting. Abrade the area immediately surrounding the repair to provide a key for subsequent coating application. Overlap areas should be kept to a minimum.

Limitations

Apply in good weather. Temperature of the surface to be coated must be least 3°C above the dew point when the is lower than 85%.

In common with all epoxy base coatings, 725-H45-ZF101G will exhibit chalking of the firm on UV exposure.

The dry time and overcoating interval may change according to the environment factors.

Avoiding absorb the solvent steam and paint steam for long time. Skin and eyes must avoid contacting the paint. Pay attention to ventilate and fireproof when applying.