High Tensile Strength PA6-G20
1.High Tensile Strength 2.low water absorption rate 3.reinforced with glass fibre
| Typical Properties | |||||||||||
| Performance | ASTM Standard | Test | Unit | PA6-101 | PA6-G10 | PA6-G20 | PA6-G30 | PA6-201FR | PA6-G20-FR | PA6-G30-FR | PA6-M30 |
| Density | D792 | 23°C | g/cm3 | 1.13 | 1.21 | 1.27 | 1.34 | 1.10 | 1.40 | 1.42 | 1.4 |
| Tensile Strength | D638 | Mpa | 75 | 105 | 115 | 130 | 70 | 110 | 130 | 80 | |
| Tensile Elongation | D638 | % | 20 | 5 | 3.8 | 3.2 | 13 | 2.5 | 3 | 10 | |
| Flexural Strength | D790 | Mpa | 110 | 155 | 175 | 220 | 108 | 190 | 210 | 125 | |
| 120D Impact Notched | D256 | KJ/m2 | 35 | 9 | 10 | 13 | 10 | 10 | 13 | 8.0 | |
| Flexural Modulus | D790 | Mpa | 2600 | 5500 | 7500 | 9000 | 3100 | 6000 | 6300 | 3200 | |
| Heat Deflection Temp | D648 | 1.82Mpa | °C | 72 | 180 | 195 | 208 | 80 | 200 | 208 | 182 |
| Rockwell Hardness | D785 | R | |||||||||
| Molding Shrinkage | D955 | % | 1.5 | 0.6/0.8 | 0.5/0.7 | 0.4/0.7 | 1.4 | 0.5/0.8 | 0.6/0.8 | 1.2 | |
| Flammability | UL-94 | 3.2mm | Class | V-2 | HB | HB | HB | V-0 | V-0 | V-0 | HB |
| Molding Conditioning | Dryness Temperature 90-100°C,Dryness Time 3--4hr,Mould Temperature60--80°C,Molding Temperature200--240°C | ||||||||||
High Tensile Strength PA6-G20