Product code

PPS-GF001

Features

Glass fiber reinforced PPS has these features:1)Good heat stability, the long-term using temperature can be 220-240°C and 

the deflection temperature under load 1.82Mpa is above 260°C;2)Good flame resistance, PPS can meet the UL94 V-0 and 5-V standard 

without any flame retardants and the amount of smoke is very little when it is burning;3)Excellent chemical resistance, better than any other plastics except PTFE, 

insoluble in any organic solvent except strong oxidizing acids.4)Very low molding shrinkage, low water absorption and linear expansion 

coefficient, keeping excellent dimensional stability even in the high temperature

 and humidity environment .

Uses

Glass fiber reinforced PPS is very widely used in many fields, because of its 

excellent comprehensive performance and good cost performance. It can be 

applied to electric, auto, train, machinery, chemistry engineering, aviation and 

aerospace, military, communication, office supplies and so on.

Test item

Test condition

Test method

Test result

Unit

Physical properties

Density

ASTM D792

1.8

g/cm3

Molding shrinkage

ASTM D955

0.2-0.4

%

The ash content of coal

ASTM D2117

40

%

Mechanical properties

Tensile strength

23°C,DAM

ASTM D638

140

Mpa

Tensile elongation

23°C,DAM

ASTM D638

6

%

Flexural strength

23°C,DAM

ASTM D790

220

Mpa

Flexural modulus

23°C,DAM

ASTM D790

12500

Mpa

Notched Izod impact(1/8") 

23°C,DAM

ASTM D256

7

KJ/m2

Thermal properties

Deflection temperature

1.82Mpa

ASTM D648

260

°C

Flammability

UL 94

V-0

—

Machining parameters 

Drying temperature

—

130-140

°C

Drying time

—

3

hr

Processing temperature

—

290-330

°C

Remarks

40% Glass fiber reinforced