Tabular Alumina Tabular alumina as catalyst support Excellent thermal volume stability High refractory,good chemical purity
Tabular Alumina
Tabular Alumina is a pure sintered α-alumina materials that has been fully densified by rapid-sintering without the use of sintering aids at temperature in excess 1900°c.
Tabular alumina has characteristic large, well developed hexagonal tablet shaped α-alumina crystals of up to 200μm length.
Features
1. low open porosity and large crystals with closed spherical pores
2. high refractoriness, high mechanical strength and abrasion resistance
3. good chemical purity, excellent dielectric properties and good resistance against acid and alkali corrosion.
Application
It is used in a variety of industries such as steel, foundry, petrochemical, ceramic and incineration.
Other common applications include its use in electrical insulators, kiln furniture and as a catalyst support.
Tabular Alumina Specification
Shape | Type | Chemical Compositon | Physical Characteristics | |||||||
Al2O3 | Na2O | SiO2 | Fe2O3 | Bulk Density | Apparent Porosity | Water Absorption | Packed Bulk Density | Cold Crushing Strength | ||
≥% | ≤% | ≤% | ≤% | ≥g/cm3 | % | % | Kg/m3 | N | ||
Ball | KPT162 | 99.7 | 0.20 | 0.02 | 0.02 | 3.65 | 1.5 | 0.4 | 2160-2000 | 2900-14700 |
KPT164 | 99.5 | 0.30 | 0.04 | 0.03 | 3.55 | 3.5 | 0.8 | 2000-1860 | 2700-13500 | |
KPT60 | 99.3 | 0.40 | 0.09 | 0.02 | 3.50 | 5 | 1.5 | |||
KPT61 | 99.1 | 0.40 | 0.13 | 0.03 | 3.45 | 6 | 2.0 | |||
Granule | KPT60G | 99.3 | 0.40 | 0.10 | 0.02 | 3.50 | 5 | 1.5 | (mm) 5-10 3-6 3-1 1-0 0.5-1 0.2-0.6 | |
KPT61G | 99.1 | 0.40 | 0.13 | 0.03 | 3.45 | 6 | 2.0 | |||
Micro Powder | KPT60P45 | 99.2 | 0.40 | 0.09 | 0.02 | 3.50 | 5 | 1.5 | (μm) -45μm (-325mesh) -20μm (-635mesh) | |
KPT60P20 | 99.1 | 0.40 | 0.15 | 0.04 | 3.50 | 5 | 1.5 | |||
KPT61P45 | 99.1 | 0.40 | 0.12 | 0.03 | 3.45 | 5 | 1.5 | |||
KPY61P20 | 99.0 | 0.40 | 0.15 | 0.04 | 3.45 | 5 | 1.5 | |||
Tabular Alumina / Aggregates